[Effect of three aging challenges on the bonding stability of resin-dentin interface using an etch-and-rinse
Shuai Xu1, Ling Zhang1, Fang Li1
1Department of Prosthodontics, College of Stomatology, The Fourth Military Medical University, Xi'an 710032, China.
Objective:
To systematically investigate the aging effect of thermocycling, water storage and bacteria aggression on the stability of resin-dentin bonds.
Methods:
Forty molars were sectioned perpendicularly to the axis of the teeth to expose the middle-coronal dentin surfaces. The dentin surfaces were then treated with Single Bond 2 and made a core build-up. According to random digits table, the bonding specimens were divided into four groups (n = 10) as follows: immediate control group, aging group with thermocycling for 5 000 times, aging group with artificial saliva storage for 6 months and aging group with bacteria aggression for 14 days. The specimens in each group were then subjected to microtensile bond strengths (µTBS) testing and nanoleakage evaluation respectively.
Results:
After aging treatments, the three aging groups showed significantly lower µTBS than the immediate control group [(44.24 ± 12.75) MPa, P < 0.05]. The immediate control group also showed the lowest value of nanoleakage. The µTBS of aging group with bacteria aggression [(25.53 ± 7.39) MPa] was significantly lower than those of the other aging groups with artificial saliva storage[(29.72 ± 6.51) MPa] and thermocycling [(31.92 ± 11.87) MPa, P < 0.05]. There were no differences in the nanoleakage values among the three aging groups (P > 0.05).
Conclusions:
All the aging treatments with artificial saliva storage, thermocycling and bacteria aggression could accelerate the degradation of bonding interfaces between an etch-and-rinse adhesive and dentin. Bacteria aggression showed the most impairing effect on the stability of resin-dentin bonds.