Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Three-dimensional quantitative analysis of adhesive remnants and enamel loss resulting from debonding orthodontic
Joanna Janiszewska-Olszowska1, Katarzyna Tandecka, Tomasz Szatkiewicz
1Department of General Dentistry Pomeranian Medical, University of Szczecin, al, Powstancow Wlkp, 72, 70-111 Szczecin, Poland. jjo@pum.edu.pl.
Aims:
Presenting a new method for direct, quantitative analysis of enamel surface. Measurement of adhesive remnants and enamel loss resulting from debonding molar tubes.
Material And Methods:
Buccal surfaces of fifteen extracted human molars were directly scanned with an optic blue-light 3D scanner to the nearest 2 μm. After 20 s etching molar tubes were bonded and after 24 h storing in 0.9% saline - debonded. Then 3D scanning was repeated. Superimposition and comparison were proceeded and shape alterations of the entire objects were analyzed using specialized computer software. Residual adhesive heights as well as enamel loss depths have been obtained for the entire buccal surfaces. Residual adhesive volume and enamel loss volume have been calculated for every tooth.
Results:
The maximum height of adhesive remaining on enamel surface was 0.76 mm and the volume on particular teeth ranged from 0.047 mm3 to 4.16 mm3. The median adhesive remnant volume was 0.988 mm3. Mean depths of enamel loss for particular teeth ranged from 0.0076 mm to 0.0416 mm. Highest maximum depth of enamel loss was 0.207 mm. Median volume of enamel loss was 0.104 mm3 and maximum volume was 1.484 mm3.
Conclusions:
Blue-light 3D scanning is able to provide direct precise scans of the enamel surface, which can be superimposed in order to calculate shape alterations. Debonding molar tubes leaves a certain amount of adhesive remnants on the enamel, however the interface fracture pattern varies for particular teeth and areas of enamel loss are present as well.