One pot aqueous synthesis of nanoporous Au85Pt15 material with surface bound Pt islands: an efficient methanol
P Anandha Ganesh1, D Jeyakumar
1Functional Materials Division, CSIR-Central Electrochemical Research Institute, Karaikkudi - 630006, Tamil Nadu, India. duraisamyjeyakumar@gmail.com.
Abstract:
For the first time, we are reporting the synthesis of Au100-xPtx nanoporous materials in the size range of 7-10 nm through the galvanic replacement of Ag by Pt from Au100-xAg2x spherical nano-alloys (x = 20, 15, 10 and 5) in an aqueous medium. The galvanic replacement reaction follows the 'Volmer-Weber' growth mode, resulting in the formation of surface bound platinum islands on a nanoporous gold surface. The high angle annular dark field image and low angle X-ray diffraction studies confirm the presence of nanoporous Au100-xPtx NPs. The electrochemical studies using the Au85Pt15/C catalyst show excellent methanol tolerance behaviour and better performance towards oxygen reduction reaction (ORR) in terms of high mass activity, mass-specific activity and figure of merit (FOM) when compared to HiSPEC Pt/C commercial catalyst. Preliminary studies on a full cell using nanoporous Au85Pt15/C (loading 1.0 mg cm(-2)) as the cathode material and Pt-Ru/C (loading: 0.5 mg cm(-2)) as the anode material performed better (38 mW cm(-2)) than the HiSPEC Pt/C cathode material (16 mW cm(-2)).