Engineering of electron-selective contact for perovskite solar cells with efficiency exceeding 15%

The past 5 years have witnessed the rise of highly efficient organometal halide perovskite-based solar cells. In conventional perovskite solar cells, compact n-type metal oxide film is always required as a blocking layer on the transparent conducting oxide (TCO) substrate for efficient electron-selective contact. In this work, an interface engineering approach is demonstrated to avoid the deposition of compact n-type metal oxide blocking film. Alkali salt solution was used to modify the TCO surface to achieve the optimized interface energy level alignment, resulting in efficient electron-selective contact. A remarkable power conversion efficiency of 15.1% was achieved under AM 1.5 G 100 mW · cm(-2) irradiation without the use of compact n-type metal oxide blocking layers.