High current density and longtime stable field electron transfer from large-area densely arrayed graphene...

Achieving high current and longtime stable field emission from large area (larger than 1 mm(2)), densely arrayed emitters is of great importance in applications for vacuum electron sources. We report here the preparation of graphene nanosheet-carbon nanotube (GNS-CNT) hybrids by following a process of iron ion prebombardment on Si wafers, catalyst-free growth of GNSs on CNTs, and high-temperature annealing. Structural observations indicate that the iron ion prebombardment influences the growth of CNTs quite limitedly, and the self-assembled GNSs sparsely distributed on the tips of CNTs with their sharp edges unfolded outside. The field emission study indicates that the maximum emission current density (Jmax) is gradually promoted after these treatments, and the composition with GNSs is helpful for decreasing the operation fields of CNTs. An optimal Jmax up to 85.10 mA/cm(2) is achieved from a 4.65 mm(2) GNS-CNT sample, far larger than 7.41 mA/cm(2) for the as-grown CNTs. This great increase of Jmax is ascribed to the reinforced adhesion of GNS-CNT hybrids to substrates. We propose a rough calculation and find that this adhesion is promoted by 7.37 times after the three-step processing. We consider that both the ion prebombardment produced rough surface and the wrapping of CNT foot by catalyst residuals during thermal processing are responsible for this enhanced adhesion. Furthermore, the three-step prepared GNS-CNT hybrids present excellent field emission stability at high emission current densities (larger than 20 mA/cm(2)) after being perfectly aged.