Synthesis of one-dimensional copper sulfide nanorods as high-performance anode in lithium ion batteries

Nanorod-like CuS and Cu2 S have been fabricated by a hydrothermal approach without using any surfactant and template. The electrochemical behavior of CuS and Cu2 S nanorod anodes for lithium-ion batteries reveal that they exhibit stable lithium-ion insertion/extraction reversibility and outstanding rate capability. Both of the electrodes exhibit excellent capacity retentions irrespective of the rate used, even at a high current density of 3200 mA g(-1) . More than 370 mAh g(-1) can be retained for the CuS electrode and 260 mAh g(-1) for the Cu2 S electrode at the high current rate. After 100 cycles at 100 mA g(-1) , the obtained CuS and Cu2 S electrodes show discharge capacities of 472 and 313 mAh g(-1) with retentions of 92% and 96%, respectively. Together with the simplicity of fabrication and good electrochemical properties, CuS and Cu2 S nanorods are promising anode materials for practical use the next-generation lithium-ion batteries.