Preparation of double emulsions using hybrid polymer/silica particles: new pickering emulsifiers with adjustable...

A facile route for the preparation of water-in-oil-in-water (w/o/w) double emulsions is described for three model oils, namely, n-dodecane, isopropyl myristate, and isononyl isononanoate, using fumed silica particles coated with poly(ethylene imine) (PEI). The surface wettability of such hybrid PEI/silica particles can be systematically adjusted by (i) increasing the adsorbed amount of PEI and (ii) addition of 1-undecanal to the oil phase prior to homogenization. In the absence of this long-chain aldehyde, PEI/silica hybrid particles (PEI/silica mass ratio = 0.50) produce o/w Pickering emulsions in all cases. In the presence of 1-undecanal, this reagent reacts with the primary and secondary amine groups on the PEI chains via Schiff base chemistry, which can render the PEI/silica hybrid particles sufficiently hydrophobic to stabilize w/o Pickering emulsions at 20 °C. Gas chromatography, (1)H NMR and X-ray photoelectron spectroscopy provide compelling experimental evidence for this in situ surface reaction, while a significant increase in the water contact angle indicates markedly greater hydrophobic character for the PEI/silica hybrid particles. However, when PEI/silica hybrid particles are prepared using a relatively low adsorbed amount of PEI (PEI/silica mass ratio = 0.075) only o/w Pickering emulsions are obtained, since the extent of surface modification achieved using this Schiff base chemistry is insufficient. Fluorescence microscopy and laser diffraction studies confirm that highly stable w/o/w double emulsions can be achieved for all three model oils. This is achieved by first homogenizing the relatively hydrophobic PEI/silica hybrid particles (PEI/silica mass ratio = 0.50) with an oil containing 3% 1-undecanal to form an initial w/o emulsion, followed by further homogenization using an aqueous dispersion of relatively hydrophilic PEI/silica particles (PEI/silica mass ratio = 0.075). Dye release from the internal aqueous cores into the aqueous continuous phase was monitored by visible absorption spectroscopy. These studies indicate immediate loss of 12-18% dye during the high speed homogenization that is required for double emulsion formation, but no further dye release is observed at 20 °C for at least 15 days thereafter.