Pressure-Sensitive Adhesives under the Influence of Relative Humidity: Inner Structure and Failure Mechanisms

Markus Schindler1, Manuel Koller1, Peter Müller-Buschbaum1

  • 1Physik-Department, Lehrstuhl für Funktionelle Materialien, Technische Universität München, James-Franck-Strasse 1, 85748 Garching, Germany.

ACS Applied Materials & Interfaces
|November 15, 2014
PubMed

Keywords:
X-ray reflectivityfailure mechanismpressure-sensitive adhesivesolution castingtack

More Related Videos

Preparation and Testing of Plant Seed Meal-based Wood Adhesives08:09

Preparation and Testing of Plant Seed Meal-based Wood Adhesives

Published on: March 5, 2015

9.2K
Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

3.6K

Related Concept Videos

Adhesion01:14

Adhesion

Adhesion occurs when one type of molecule is attracted to a different molecule. Water exhibits adhesive properties in the presence of polar surfaces, such as glass or cellulose in plants. For instance, when water is poured into a glass, the positively charged hydrogen molecules of water are more attracted to the negatively charged oxygen molecules in the silica than to the oxygen in neighboring water molecules.
Capillary action is a result of water’s adhesive tendencies. When a narrow...
45.6K
Drying Shrinkage01:21

Drying Shrinkage

When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
A portion of this drying shrinkage can be reversed; if the concrete is...
490
Surface Tension, Capillary Action, and Viscosity02:57

Surface Tension, Capillary Action, and Viscosity

Surface Tension
The various IMFs between identical molecules of a substance are examples of cohesive forces. The molecules within a liquid are surrounded by other molecules and are attracted equally in all directions by the cohesive forces within the liquid. However, the molecules on the surface of a liquid are attracted only by about one-half as many molecules. Because of the unbalanced molecular attractions on the surface molecules, liquids contract to form a shape that minimizes the number...
34.9K
Tension Response at Adherens Junctions01:26

Tension Response at Adherens Junctions

The adherens junctions that anchor cells together are multi-protein complexes that dynamically adapt to mechanical stimuli such as tensile forces and shear stress. Mechanosensory proteins in these junctions can sense such mechanical stimuli and undergo a shift in their conformation, resulting in an altered function — a process called mechanotransduction.
α-Catenin as a Mechanosensory Protein
The α-catenin of adherens junctions is an allosteric protein with three VH (vinculin...
4.3K
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
1.0K