Polyethylenimine aqueous solution: a low-cost and environmentally friendly formulation to produce low-work-function
Xue Min1, Fangyuan Jiang, Fei Qin
1Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology , Wuhan 430074, China.
Abstract:
Polyethylenimine (PEI) has been widely used to produce low-work-function electrodes. Generally, PEI modification is prepared by spin coating from 2-methoxyethanol solution. In this work, we explore the method for PEI modification on indium tin oxide (ITO) by dipping the ITO sample into PEI aqueous solution for organic solar cells. The PEI prepared in this method could reduce the work function of ITO as effectively as PEI prepared by spin coating from 2-methoxyethanol solution. H2O as the processing solvent is more environmentally friendly and much cheaper compared to the 2-methoxyethanol solvent. The dipping method is also compatible with large-area samples. With low-work-function ITO treated by the dipping method, solar cells with a simple structure of glass/ITO/PEI(dipping)/P3HT:ICBA/PEDOT:PSS(vacuum-free processing) display a high open-circuit voltage of 0.86 ± 0.01, a high fill factor of 66 ± 2%, and power conversion efficiency of 4.4 ± 0.3% under 100 mW/cm(2) illumination.
More Related Videos
08:29Morphology Control for Fully Printable Organic–Inorganic Bulk-heterojunction Solar Cells Based on a Ti-alkoxide and Semiconducting Polymer
Published on: January 10, 2017
10:48Electrochemical Preparation of Poly3,4-Ethylenedioxythiophene Layers on Gold Microelectrodes for Uric Acid-Sensing Applications
Published on: July 28, 2021