Synthesis, structure, crystal growth and characterization of a novel semiorganic nonlinear optical l-proline lithium...

l-Proline lithium bromide monohydrate (LPLBM), a promising semiorganic nonlinear optical material, was synthesized and single crystals of LPLBM were grown from solution by slow evaporation technique. Single crystal X-ray structure solution reveals that the grown crystal belongs to monoclinic system with space group P21. Presence of various functional groups was identified by FT-IR and FT-Raman spectral analyses. UV-Vis-NIR spectroscopic study shows that the LPLBM crystal possesses 90% of transmittance in the range of 250-1100nm. Vickers microhardness values, the dielectric constant and dielectric loss of the LPLBM crystal were reported. Elemental analysis by energy dispersive X-ray analysis shows the presence of carbon, nitrogen, oxygen and bromine. The surface morphology of the crystal was investigated using scanning electron microscopic study. The thermal stability of the LPLBM crystal was studied from TGA and DSC analysis. Second harmonic generation efficiency of the LPLBM crystal measured by Kurtz and Perry powder technique using Nd:YAG laser is about 0.3 times that of urea.