Carbon nanotubes reinforced poly(L-lactide) scaffolds fabricated by thermally induced phase separation

In tissue engineering, porous nanocomposite scaffolds can potentially mimic aspects of the nanoscale architecture of the extra-cellular matrix, as well as enhance the mechanical properties required for successful weight-bearing implants. In this paper, we demonstrate that highly porous thermoplastic poly(L-lactide) nanocomposite scaffolds containing different types of functionalized multi-walled carbon nanotubes (CNTs). The nanocomposite scaffolds were manufactured by a thermally induced phase separation method. This experiment produced an uniform distribution of CNTs throughout the scaffold without obvious aggregations for funtionalized CNTs filled scaffolds by scanning electron microscope observation. The CNTs were frequently located on the pore surface, forming rough, hairy nano-textures. The pore size was reduced with the increasing of CNT loading. Parts of PLLA matrix was induced into nanofibrous structures from solid-walled state, which reduced the crystallinity of the PLLA characterized by DSC measurement. The CNT incorporation significantly improved the compression modulus of the nanocomposite scaffolds, especially the functionalized CNTs. The capacity of protein adsorption is significantly improved when the concentration of the CNTs was higher than 1.0 wt.% and the cell attachment was also enhanced by the addition of CNTs, especially N-CNT.