Effect of Desensitizing Agents on the Bond Strength of Mild and Strong Self-etching Adhesives
Background:
Desensitizing agents are used, almost as routine practice, in many adhesive restorative procedures. There is still debate as to their effect in dentin bonding, particularly with self-etching adhesives. The present study aimed to evaluate the effect of different desensitizing agents on the bond strength of mild and strong self-etching adhesive systems to dentin.
Materials And Methods:
One hundred twenty recently extracted, noncarious human molars were used to obtain superficial dentin substrate for bonding. No desensitizer was used in the control groups. The experimental groups were pretreated with Gluma Desensitizer, MicroPrime B, and Dentin Desensitizer immediately prior to bonding with self-etching adhesives Optibond XTR, Xeno IV, and iBond. A bonding jig was used to fabricate composite cylinders, which were stored for either 24 hours or three months, after which the shear bond strength (SBS) was evaluated using a notched-edge testing device at a crosshead speed of 1 mm/min. Failure mode distribution was also evaluated at 24 hours and three months. A two-way analysis of variance, Tukey test, and Student t-test, with a significance level of p<0.05, were used for data analysis.
Results:
At 24 hours, there was no significant difference in SBS when the same adhesive was used with any of the experimental desensitizing agents compared with the control group without desensitizer. However, at three months, Dentin Desensitizer bonded with Optibond XTR demonstrated significantly lower SBS (p<0.001), while Gluma bonded with iBond showed significantly higher SBS values (p=0.034) relative to their corresponding control group. Only MicroPrime B bonded with Xeno IV and iBond with no desensitizer demonstrated a significant reduction in SBS after three months (p=0.034 and p=0.002, respectively). The most prevalent type of failure was adhesive.
Conclusion:
Desensitizing agents can be used in combination with self-etching adhesives to control hypersensitivity without adversely affecting their bond strength to dentin.
Related Concept Videos
01:19Masking and Demasking Agents
There are many masking agents, such as cyanide, fluoride, triethanolamine, thiourea, and 2,3-bis(sulfanyl)propan-1-ol (formerly 2,3-dimercapto-1-propanol), with the masking agent chosen based on...
01:12Bonding and Strength of Aggregate
01:29Leveling Effect
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...
01:19Ionic Strength: Effects on Chemical Equilibria
In this solution, the primary...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with...