Ultrasonic mediated synthesis of monodispersed lanthanum hydroxide nanorods for possible bioimplant application

Monodispersed lanthanum hydroxide nano-rods (LaNRs) were synthesized for prospective biomedical application using a microwave heating and ultrasonic agitation methodology which does not require any toxic stabilizing agent. The average length and diameter of the LaNRs thus obtained were 183.4 ± 3.6 and 9.9 ± 0.2 nm respectively, as analyzed by HRTEM. FTIR spectrum confirmed the presence of OH groups. The thermal transformation of lanthanum hydroxide (La(OH)3) was studied by thermogravimetric analysis. The synthesized LaNRs were found to be stable for a period of 1 month at room temperature. They were biocompatible as evaluated by haemocompatibility assay and viability assay using human peripheral blood mononuclear cells. The pro-angiogenic property of LaNRs was demonstrated by in vivo chick chorioallantoic membrane assay. The LaNRs induced osteoblast differentiation of human adipose derived stem cells with significant calcium (Ca(2+)) deposition indicating potential applications in bone tissue engineering.