Imaging the effects of annealing on the polymorphic phases of poly(vinylidene fluoride)

The effect of annealing on the phase transformation and the dielectric properties of poly(vinylidene fluoride) (PVDF) is explored using quasi-single molecule (quasi-SM) microscopy. The solvatochromic properties of nile red (NR) are employed to measure the spatial distribution of the local dielectric constant (ε) in ∼30 μm thick PVDF films before and after annealing at 90 °C. The results presented here demonstrate that nonannealed films exhibit much larger ε distributions, both in terms of magnitude and distribution, when compared to annealed films. The polymorphic phase of PVDF before and after annealing is also confirmed using X-ray diffraction. Nonannealed films are found to be in the γ-phase with annealing promoting the transition to primarily β-phase. Combining these results, we conclude that the decrease in ε with annealing time is due to the phase transformation from γ- to β-phase. Using quasi-SM imaging techniques one can readily visualize the ε environments present within different polymorphic phases of PVDF.