Tailoring of the titanium surface by preparing cardiovascular endothelial extracellular matrix layer on the
Jingan Li1, Kun Zhang2, Juejue Wu1
1Key Laboratory for Advanced Technologies of Materials, Ministry of Education, School of Material Science and Engineering, Southwest Jiaotong University, Chengdu 610031, PR China.
Abstract:
It has been proved that high molecular weight hyaluronic acid (HMW-HA, 1×10(6) Da) micro-strips on titanium (Ti) surface can elongate the human vascular endothelial cell (EC) morphology, subsequently enhance endothelial extracellular matrix (ECM) deposition in our previous work. The HMW-HA micro-strips were anticipated to possess good hemocompatibility and EC compatibility simultaneously. However, the single HMW-HA micro-strips on Ti substrate showed bad hemocompatibility. To solve this problem, a method combining HA micro-pattern and EC decellularization was developed, and the endothelial extracellular matrix layer on the HA micro-pattern (ECM/HAP) showed excellent hemocompatibility and endothelial progenitor cells (EPCs) compatibility (cell number: 14.3±0.5×10(5) cells/cm2>2.2±0.7×10(5) cells/cm2 on ECM/TiOH, 7.5±1.3×10(5) cells/cm2 on TiOH, 3.4±0.9×10(5) cells/cm2 on TiOH/HAP and 3.6±1.2×10(5) cells/cm2 on Ti). We also found that the ECM/HAP coating could significantly inhibit the excessive proliferation of smooth muscle cells (SMCs) (cck-8 absorption: 0.25±0.06<1.18±0.09 A.U. on ECM/TiOH, 0.87±0.15 A.U. on TiOH and 1.55±0.11 A.U. on Ti) and the attachment of macrophages (cell number: 1.3±0.1×10(3)<9.2±1.5×10(3) cells/cm2 on ECM/TiOH, 8.8±0.3×10(3) cells/cm2 on TiOH, 7.3±0.7×10(3) cells/cm2 on TiOH/HAP and 9.6±0.9×10(3) cells/cm2 on Ti in 12 h). These data suggest that the multifunctional ECM/HAP coating can be used to build the bionic human endothelial ECM on the biomaterials surface, which might provide a potential and effective method for surface modification of cardiovascular devices.