A thermodynamic analysis of the amorphous to crystalline calcium phosphate transformation

A thermodynamic analysis of the precipitation of amorphous calcium phosphate (ACP) and its transformation to crystalline apatite had been made. A nearly constant ion product, over a wide variety of conditions, was obtained for a tricalcium phosphate (TCP)-like phase suggesting that the molecular unit which governs the solubility of ACP may be similar in composition to TCP. The introduction of 10% acid phosphate into the formula for the TCP ion product improves the fit of experimental data and results in an invariant ion product. The stability of ACP in solution was found to be dependent upon its thermodynamic instability with respect to an octacalcium phosphate (OCP)-like phase. The dependence of the induction period for the amorphous to crystalline transformation upon the pH and the Ca/P ratio of the solution is best explained by the assumption that an OCP-like phase is initially nucleated on the surfaces of the ACP particles. The events that occur in the immediate post-transition period suggest the hydrolysis of this OCP-like material to an apatitic phase.