Pt@UiO-66 heterostructures for highly selective detection of hydrogen peroxide with an extended linear range

In this study, a good core-shell heterostructure of Pt NPs@UiO-66 was fabricated by encapsulating presynthesized platinum nanoparticles (Pt NPs) into the host matrix of UiO-66 which possesses the slender triangular windows with a diameter of 6 Å. The transmission electron microscopy images exhibited that the number of the encapsulated Pt NPs and the crystalline morphology of as-synthesized core-shell heterostructure samples had a series of changes with increasing the volume of the injected Pt NPs precursor solution. Among these samples, the Pt NPs@UiO-66-2 sample had a good crystalline morphology with several well-dispersed Pt NPs encapsulated in UiO-66 frameworks. But there were no obvious Pt NPs observed in the Pt NPs@UiO-66-1 sample, and for the Pt NPs@UiO-66-3 sample, the number of Pt NPs encapsulated in UiO-66 matrix notably reduced and the metal organic framework (MOF) crystals became small and aggregated. The electrochemical measurements showed that the Pt NPs@UiO-66-2 sample modified glass carbon electrode (GCE) presented a remarkable electrocatalytic activity toward hydrogen peroxide (H2O2) oxidation, including an excellent anti-interference performance even if the concentration of the interference species was the same as the H2O2, an extended linear range from 5 μM to 14.75 mM, a low detection limit, as well as good stability and reproducibility. The results indicate the superiority of MOFs in H2O2 detection. And more importantly, it will provide a new opportunity to promote the anti-interference performance of the nonenzyme electrochemical sensors.