Transparent nanotubular capacitors based on transplanted anodic aluminum oxide templates

Transparent AlZnO/Al2O3/AlZnO nanocapacitor arrays have been fabricated by atomic layer deposition in anodic aluminum oxide templates transplanted on the AlZnO/glass substrates. A high capacitance density of 37 fF/μm(2) is obtained, which is nearly 5.8 times bigger than that of planar capacitors. The capacitance density almost remains the same in a broad frequency range from 1 kHz to 200 kHz. Moreover, a low leakage current density of 1.7 × 10(-7) A/cm(2) at 1 V has been achieved. The nanocapacitors exhibit an average optical transmittance of more than 80% in the visible range, and thus open the door to practical applications in transparent integrated circuits.