Development of an activated carbon filter to remove NO2 and HONO in indoor air

To obtain the optimum removal efficiency of NO2 and HONO by coated activated carbon (ACs), the influencing factors, including the loading rate, metal and non-metal precursors, and mixture ratios, were investigated. The NOx removal efficiency (RE) for K, with the same loading (1.0 wt.%), was generally higher than for those loaded with Cu or Mn. The RE of NO2 was also higher when KOH was used as the K precursor, compared to other K precursors (KI, KNO3, and KMnO4). In addition, the REs by the ACs loaded with K were approximately 38-55% higher than those by uncoated ACs. Overall, the REs (above 95%) of HONO and NOx with 3% KOH were the highest of the coated AC filters that were tested. Additionally, the REs of NOx and HONO using a mixing ratio of 6 (2.5% PABA (p-aminobenzoic acid)+6% H3PO4):4 (3% KOH) were the highest of all the coatings tested (both metal and non-metal). The results of this study show that AC loaded with various coatings has the potential to effectively reduce NO2 and HONO levels in indoor air.