Reactivity of zirconia with phosphate-bonded investments for hot-pressing

Kentaro Yoshihara1, Yoshinori Nakamura1, Seiji Ban2

  • 1Department of Removable Prosthodontics, School of Dentistry, Aichi Gakuin University, 2-11 Suemori-dori, Chikusa-ku, Nagoya, Japan.

Journal of Prosthodontic Research
|March 10, 2015
PubMed
Abstract

Keywords:
Biaxial flexural strengthPhosphate-bonded investmentShear bond strengthZirconia

More Related Videos

Fused Filament Fabrication FFF of Metal-Ceramic Components08:43

Fused Filament Fabrication FFF of Metal-Ceramic Components

Published on: January 11, 2019

18.3K
Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)08:29

Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)

Published on: January 7, 2019

12.0K

Related Concept Videos

α-Bromination of Carboxylic Acids: Hell–Volhard–Zelinski Reaction01:15

α-Bromination of Carboxylic Acids: Hell–Volhard–Zelinski Reaction

The method to achieve α-brominated carboxylic acids using a mixture of phosphorus tribromide and bromine is known as the Hell–Volhard–Zelinski reaction. The reaction is catalyzed by phosphorus tribromide, which can be used directly or produced in situ from red phosphorus and bromine. The mechanism comprises PBr3 catalyzed conversion of acid to acid bromide and hydrogen bromide. The acid bromide enolizes to its enol form in the presence of HBr. The nucleophilic enol attacks the...
4.0K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
879
Pozzolans01:21

Pozzolans

Pozzolans are siliceous or aluminous materials blended with Portland cement. They interact with the calcium hydroxide produced during the hydration of Portland cement and contribute to improved strength and durability of concrete. The pozzolanic activity, a measure of a pozzolan's effectiveness, is typically assessed using the strength activity index, as defined in ASTM C 618-93, which calculates the ratio of the compressive strength of cement mixtures with and without pozzolan.
Fly ash is...
782