Anodic WO3 mesosponge @ carbon: a novel binder-less electrode for advanced energy storage devices

A novel design for an anodic WO3 mesosponge @ carbon has been introduced as a highly stable and long cyclic life Li-ion battery electrode. The nanocomposite was successfully synthesized via single-step electrochemical anodization and subsequent heat treatment in an acetylene and argon gas environment. Morphological and compositional characterization of the resultant materials revealed that the composite consisted of a three-dimensional interconnected network of WO3 mesosponge layers conformally coated with a 5 nm thick carbon layer and grown directly on top of tungsten metal. The results demonstrated that the carbon-coated mesosponge WO3 layers exhibit a capacity retention of 87% after completion of 100 charge/discharge cycles, which is significantly higher than the values of 25% for the crystalline (without carbon coating) or 40% for the as-prepared mesosponge WO3 layers. The improved electrochemical response was attributed to the higher stability and enhanced electrical conductivity offered by the carbon coating layer.