Testing of action of direct flame on concrete

Lenka Bodnarova1, Jaroslav Valek1, Petr Novosad1

  • 1Faculty of Civil Engineering, Brno University of Technology, Institute of Technology of Building Materials and Components, Veveri 331/95, 602 00 Brno, Czech Republic.

Thescientificworldjournal
|April 2, 2015
PubMed

More Related Videos

Experimental Procedure for Laboratory Studies of In Situ Burning : Flammability and Burning Efficiency of Crude Oil12:34

Experimental Procedure for Laboratory Studies of In Situ Burning : Flammability and Burning Efficiency of Crude Oil

Published on: May 1, 2018

13.2K
Assessing Disaster Resilience of Concrete with Titanium Dioxide Nanoparticles05:45

Assessing Disaster Resilience of Concrete with Titanium Dioxide Nanoparticles

Published on: November 14, 2025

509

Related Concept Videos

Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
766
Impact Strength of Concrete01:21

Impact Strength of Concrete

Impact strength in concrete is a critical measure that reflects the material's capability to endure the forces applied during pile driving and when supporting machinery foundations that experience impulsive loads. It is also essential when handling precast concrete components to prevent accidental damage. The impact strength is assessed by observing the concrete's resistance to repeated impacts and energy absorption capacity. A key indicator of significant damage to concrete is when it...
721
Flame Photometry: Lab01:16

Flame Photometry: Lab

In a flame photometer, when a solution like potassium chloride is aspirated into the flame, the solvent evaporates, leaving behind dehydrated salt. This salt dissociates into free gaseous atoms in their ground state. Some of these atoms absorb energy from the flame, leading to their excitation. The excited atoms return to the ground state, emitting photons at characteristic wavelengths. Because only electronic transitions are involved, the resulting emission lines are very narrow. The intensity...
1.3K
Hot Weather Concreting01:20

Hot Weather Concreting

Concreting at elevated temperatures accelerates the hydration process, leading to quicker setting but potentially reducing the long-term strength of the concrete structure. Additionally, low air humidity fosters rapid moisture loss from the concrete, resulting in reduced workability, pronounced plastic shrinkage, and a higher likelihood of crazing.
Mitigating the heat increase in concrete can be economically achieved by shading aggregate stockpiles to prevent heating from solar radiation,...
376
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
712
Mass Concreting01:22

Mass Concreting

Mass concreting refers to the process of placing large volumes of concrete, such as in gravity dams. The heat generated during the cement hydration process and differential cooling rates within the concrete mass can lead to a temperature gradient, which can result in thermal cracks in the concrete mass.
To reduce the risk of such cracking, the concrete mix may incorporate low-heat cement and pozzolans to reduce the temperature rise. Pre-cooled angular aggregates and water-reducing admixtures...
478