A poly(lactide-co-glycolide) film loaded with abundant bone morphogenetic protein-2: A substrate-promoting osteoblast...

We explored a novel biodegradable poly(lactide-co-glycolide) (PLGA) film loaded with over 80 wt % bone morphogenetic protein (BMP)-2, which was regarded as a substrate-promoting osteoblast attachment, proliferation, and differentiation for application of bone tissue engineering. Using phospholipid as a surfactant, BMP-2 was modified as a complex (PBC) for dispersing in PLGA/dichloromethane solution. The PLGA film loaded with BMP-2 and phospholipid complex (PBC-PF) showed rough and draped morphology with high entrapment efficiency exceeding 80% and good hydrophilicity, respectively. The in vitro release study of BMP-2 showed that about 50% BMP-2 was slowly and continuously released from PBC-PF within 5 weeks and had a short initial burst release only in the last 1.5 days, which was better than serious burst release of PLGA film loaded with pure BMP-2 without phospholipid (BMP-PF) as control. By comparison with other PLGA films and tissue culture plates, it was confirmed that PBC-PF significantly promoted the attachment, proliferation, and differentiation of osteoblasts with higher entrapment efficiency and better sustained release. These advantages illustrated that PBC-PF could be a potential substrate providing long-term requisite growth factors for osteoblasts, which might be applied in bone tissue engineering.