Wet Chemistry and Peptide Immobilization on Polytetrafluoroethylene for Improved Cell-adhesion
Published on: August 15, 2016
Development of a Polyester Coating Combining Antithrombogenic and Cell Adhesive Properties: Influence of Sequence and
Samantha Noel1, Ahmed Hachem2, Yahye Merhi2
1†Department of Chemical Engineering, Groupe de Recherche en Sciences et Technologies Biomédicales, Bio-P2 Research Unit, École Polytechnique de Montréal, P.O. Box 6079, succ. Centre-Ville, Montréal (QC), Canada H3C 3A7.
Abstract:
Biofunctionalization strategies have been developed to improve small-diameter vascular grafts. However, a fully successful coating featuring antithrombogenic properties while allowing for endothelialization has not been achieved yet. In this report, we explored the combination of low-fouling polyethylene glycol (PEG) and adhesion peptides, namely, RGD, YIGSR, and REDV, grafted on top of polyvinylamine (PVAm)-coated polyester. The peptides were grafted over a wide range of density (ca. 20-2000 pmol/cm(2)) on top of a dense PEG underlayer. The coating performances were assessed through HUVEC adhesion, platelet attachment, and protein adsorption, which were all drastically diminished on PEG-coated samples. RGD exhibited the expected high adhesive properties, toward both HUVEC and platelets. REDV had no effect neither on platelet attachment, as expected, nor on HUVEC adhesion, in contrast with previous reports. YIGSR was the most promising sequence even though its combination with other agents should be explored to further decrease thrombogenicity for vascular graft applications.