Magnesium modification of a calcium phosphate cement alters bone marrow stromal cell behavior via an...

The chemical composition, structure and surface characteristics of biomaterials/scaffold can affect the adsorption of proteins, and this in turn influences the subsequent cellular response and tissue regeneration. With magnesium/calcium phosphate cements (MCPC) as model, the effects of magnesium (Mg) on the initial adhesion and osteogenic differentiation of bone marrow stromal cells (BMSCs) as well as the underlying mechanism were investigated. A series of MCPCs with different magnesium phosphate cement (MPC) content (0∼20%) in calcium phosphate cement (CPC) were synthesized. MCPCs with moderate proportion of MPC (5% and 10%, referred to as 5MCPC and 10MCPC) were found to effectively modulate the orientation of the adsorbed fibronectin (Fn) to exhibit enhanced receptor binding affinity, and to up-regulate integrin α5β1 expression of BMSCs, especially for 5MCPC. As a result, the attachment, morphology, focal adhesion formation, actin filaments assembly and osteogenic differentiation of BMSCs on 5MCPC were strongly enhanced. Further in vivo experiments confirmed that 5MCPC induced promoted osteogenesis in comparison to ot her CPC/MCPCs. Our results also suggested that the Mg on the underlying substrates but not the dissolved Mg ions was the main contributor to the above positive effects. Based on these results, it can be inferred that the specific interaction of Fn and integrin α5β1 had predominant effect on the MCPC-induced enhanced cellular response of BMSCs. These results provide a new strategy to regulate BMSCs adhesion and osteogenic differentiation by adjusting the Mg/Ca content and distribution in CPC, guiding the development of osteoinductive scaffolds for bone tissue regeneration.