Across plane ionic conductivity of highly oriented neodymium doped ceria thin films

A methodology to limit interfacial effects in thin films is proposed and explained. The strategy is to reduce the impact of the electrode interfaces and eliminate cross grain boundaries that impede ionic motion. To this end, highly oriented Nd0.1Ce0.9O2-δ (NDC) nanocrystalline thin films were grown using pulsed laser deposition (PLD) on platinized single crystal a-plane sapphire substrates. High resolution cross-sectional transmission electron microscopy (HR-XTEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) verified the films were textured with columnar grains. The average widths of the columns were approximately 40 nm and not significantly changed by film thickness between 100 and 300 nm. HR-XTEM and XRD determined the {111} planes of NDC were grown preferentially on top of the {111} planes of platinum despite the large lattice mismatch between the two planes. From the XRD patterns, the out of plane strains on the platinum and NDC layers were less than 1%. This can be explained by the coincident site lattice (CSL) theory. Rotating the {111} ceria planes 19.11° with respect to the {111} platinum planes forms a Σ7 boundary where 1 in 7 cerium lattice sites are coincident with the platinum lattice sites. This orientation lowers interfacial energy promoting the preferential alignment of those two planes. The across plane ionic conductivity was measured at low temperatures (<350 °C) for the various film thicknesses. It is here shown that columnar grain growth of ceria can be induced on platinized substrates allowing pathways that are clear of blocking grain boundaries that cause conductivities to diminish as film thickness decreases.