Viscoelastic properties of sterically stabilised emulsions and their stability

The interaction forces between emulsion droplets containing adsorbed polymeric surfactants and the theory of steric stabilisation are briefly described. The results for the viscoelastic properties of O/W emulsions that are stabilised with partially hydrolysed poly(vinyl acetate) that is commonly referred to as poly(vinyl alcohol) (PVA) with 4% vinyl acetate are given. The effect of the oil volume fraction, addition of electrolytes and increasing temperature is described. This allows one to obtain various parameters such as the adsorbed layer thickness, the critical flocculation concentration of electrolyte (CFC) and critical flocculation temperature (CFT) at constant electrolyte concentration. The viscoelastic properties of O/W emulsions stabilised with an A-B-A block copolymer of polyethylene oxide (A) and polypropylene oxide (B) are described. These emulsions behave as viscoelastic liquids showing a cross-over-point between G' (the elastic component of the complex modulus) and G″ (the viscous component of the complex modulus) at a characteristic frequency. Plots of G' and G″ versus oil volume fraction ϕ show the transition from predominantly viscous to predominantly elastic response at a critical volume fraction ϕ(c). The latter can be used to estimate the adsorbed layer thickness of the polymeric surfactants. Results are also shown for W/O emulsions stabilised with an A-B-A block copolymer of polyhydroxystearic acid (PHS, A) and polyethylene oxide (PEO, B). The viscosity volume fraction curves could be fitted to the Dougherty-Krieger equation for hard-spheres. The results could be applied to give an estimate of the adsorbed layer thickness Δ which shows a decrease with increase of the water volume fraction. This is due to the interpenetration and/or compression of the PHS layers on close approach of the water droplets on increasing the water volume fraction. The last section of the review gives an example of O/W emulsion stability using an AB(n) graft copolymer of polyfructose (A) to which several C12 alkyl chains are grafted. The emulsions are stable both at high temperature and in the presence of high electrolyte concentrations (2 mol dm(-3) NaCl). This high stability is due to the strong adsorption ("anchoring") of the graft copolymer with several C12 alkyl chains and the strong hydration of the polyfructose chains both in water and in the presence of high electrolyte concentrations and temperature. Evidence for this high stability is obtained using disjoining pressure measurements which show a highly stable film between the emulsion droplets and absence of its rupture up to high pressures.