The influence of stem taper re-use upon the failure load of ceramic heads

Julian Gührs1, Annika Krull1, Florian Witt1

  • 1TUHH Hamburg University of Technology, Denickestrasse 15, 21073 Hamburg, Germany.

Medical Engineering & Physics
|April 25, 2015
PubMed

Keywords:
Ceramic bearingsFracture loadHead-taper connectionStem taper re-useTotal hip replacementhip implant failureceramic implant strengthstem taper reuseimplant revision surgery

More Related Videos

Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

1.5K
Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

956

Related Concept Videos

Normal Strain under Axial Loading01:20

Normal Strain under Axial Loading

Normal strain under axial loading is an important concept in the field of mechanics of materials. Axial loading implies the application of a force along the axis of a material, like a column or bar. This force can either compress or stretch the material. In the context of axial loading, normal strain is the deformation experienced by the material in the direction of the loading force. It's calculated as the change in length divided by the original length of the material. This unitless ratio...
1.6K
Thin-Walled Hollow Shafts01:15

Thin-Walled Hollow Shafts

In analyzing a thin-walled hollow shaft subjected to torsional loading, a segment with width dx is isolated for examination. Despite its equilibrium state, this segment faces torsional shearing forces at its ends. These forces are quantitatively described by the product of the longitudinal shearing stress on the segment's minor surface and the area of this surface, leading to the concept of shear flow. This shear flow is consistent throughout the structure, indicating a uniform distribution of...
699
Residual Stresses in Circular Shafts01:10

Residual Stresses in Circular Shafts

In materials that exhibit elastic and plastic behavior, known as elastoplastic materials, residual stresses can accumulate when these materials experience plastic deformation. This deformation arises from either high levels of shearing stress or significant strains. Residual stresses are internal stresses that persist within a material after removing the external force causing deformation. This phenomenon is demonstrated when observing the behavior of a shaft under torque; notably, the...
642
Stresses under Combined Loadings01:23

Stresses under Combined Loadings

When analyzing a bent tube with a circular cross-section subjected to multiple forces, it is crucial to determine the stress distribution in order to maintain structural integrity under varied load conditions.
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...
555
General Case of Eccentric Axial Loading01:12

General Case of Eccentric Axial Loading

Unsymmetrical bending occurs when the bending moment applied to a structural member does not align with its principal axis. This misalignment leads to complex stress distributions and deflection patterns that differ from symmetrical bending, which are essential for designing structures to withstand different loading conditions.
Consider a member subjected to equal and opposite forces that are applied along a line that does not coincide with the member's neutral axis. In unsymmetrical...
631
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
1.2K