Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells
08:30

Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells

Published on: March 19, 2017

17.3K

Planar CH3NH3PbI3 Perovskite Solar Cells with Constant 17.2% Average Power Conversion Efficiency Irrespective of the

Jin Hyuck Heo1, Dae Ho Song1, Hye Ji Han1

  • 1Functional Crystallization Center (FCC), Department of Chemical Engineering, Kyung Hee University, 1732 Deogyeong-daero, Giheung-gu, Yongin-si, Gyeonggi-do, 446-701, Republic of Korea.

Advanced Materials (Deerfield Beach, Fla.)
|April 28, 2015
PubMed
Abstract

No abstract available in PubMed .

Keywords:
crystallizationhybrid solar cellsmethylammoniumleadtribromideperovskitesolubility

More Related Videos

Low Pressure Vapor-assisted Solution Process for Tunable Band Gap Pinhole-free Methylammonium Lead Halide Perovskite Films08:12

Low Pressure Vapor-assisted Solution Process for Tunable Band Gap Pinhole-free Methylammonium Lead Halide Perovskite Films

Published on: September 8, 2017

10.2K
Influence of Hybrid Perovskite Fabrication Methods on Film Formation, Electronic Structure, and Solar Cell Performance11:38

Influence of Hybrid Perovskite Fabrication Methods on Film Formation, Electronic Structure, and Solar Cell Performance

Published on: February 27, 2017

19.2K

Related Concept Videos

P-N junction01:11

P-N junction

A p-n junction is formed when p-type and n-type semiconductor materials are joined together. At the interface of the p-n junction, holes from the p-side and electrons from the n-side begin to diffuse into the opposite sides due to the concentration gradient. This diffusion of carriers leads to a region around the junction where there are no free charge carriers, known as the depletion region. The charge density within the depletion region for the n-side and p-side can be described by the...
1.7K