Coating lithium titanate with nitrogen-doped carbon by simple refluxing for high-power lithium-ion batteries

Nitrogen-doped carbon is coated on lithium titanate (Li4Ti5O12, LTO) via a simple chemical refluxing process, using ethylenediamine (EDA) as the carbon and nitrogen source. The process incorporates a carbon coating doped with a relatively high amount of nitrogen to form a conducting network on the LTO matrix. The introduction of N dopants in the carbon matrix leads to a higher density of C vacancies, resulting in improved lithium-ion diffusion. The uniform coating of nitrogen-doped carbon on Li4Ti5O12 (CN-LTO) enhances the electronic conductivity of a CN-LTO electrode and the corresponding electrochemical properties of the cell employing the electrode. The results of our study demonstrate that the CN-LTO anode exhibits higher rate capability and cycling performance over 100 cycles. From the electrochemical tests performed, the specific capacity of CN-LTO electrode at higher rates of 20 and 50 C are found to be 140.7 and 82.3 mAh g(-1), respectively. In addition, the CN-Li4Ti5O12 anode attained higher capacity retention of 100% at 1 C rate after 100 cycles and 92.9% at 10 C rate after 300 cycles.