TiO2/bi A-SPAES(Ds 1.0) composite membranes for proton exchange membrane in direct methanol fuel cell (DMFC)

A series of TiO2/bi A-SPAES(Ds 1.0) composite membranes with various contents of nano-sized TiO2 particles were prepared through sol-gel method. Scanning electron microscopy (SEM) images indicated the TiO2 particles were well dispersed within polymer matrix. These membranes were used for proton exchange membrane (PEM) for performance evaluation in direct methanol fuel cell (DMFC). These composite membranes showed good thermal stability and mechanical strength. It was found that the water uptake of these membranes enhanced with the TiO2 amount increasing in these composite membranes. Meanwhile, the introduction of TiO2 particles increased the proton conductivity and reduced the methanol permeability. The proton conductivities of these composite membranes with 8% TiO2 particles (0.120 S/cm and 0.128 S/cm) were higher than those of Nafion 117 membrane (0.114 S/cm and 0.117 S/cm) at 80 degrees C and 100 degrees C. Specially, the methanol diffusion coefficient (1.2 x 10(-7) cm2/s) of the composite membrane with 8% TiO2 content was much lower than that of Nafion 117 membrane (2.1 x 10(-6) cm2/s). As a result, the TiO2/bi A-SPAES composite membrane was considered as a promising material for PEM in DMFC.