Band gap control using electric field of photonic gel cells fabricated with block copolymer and hydrogel

Optical and electrical characteristics of the devices using photonic gel film and hydrogel electrolyte were studied. Poly(styrene-b-2-vinylpyridine) (PS-b-P2VP) lamellar film with alternating hydrophobic block and hydrophilic polyelectrolyte block polymers (52 kg/mol-b-57 kg/mol) were prepared for the photonic gel. Poly(isobutylene-co-maleic acid) sodium salts were prepared for the hydrogel. This hydrogel fiber is common water swelling material and it owned ions for a device has conductivity. Photonic gel and hydrogel was spin coating onto Indium-tin-oxide (ITO) glass for make electric fields. The reflectance maximum wavelength of photonic crystal device shifted from 538 nm and reached to 557 nm, 585 nm and 604 nm during 30 min voltage applying time. The bandwidth variation was very limited. Loss of electrolyte was much less with hydrogel compared to the pure water. We can control color of hydrogel used photonic device by electric field with reasonable time range under moderate electric field by applying 2 V between two facing electrodes.