Nanotube nucleation phenomena on Ti-25Ta-xZr alloys for implants using ATO technique

The purpose of this study was to investigate nanotube nucleation phenomena on the Ti-25Ta-xZr alloys for implant materials, using an anodic titanium oxide (ATO) technique. Ti-25Ta-(0 wt.%-15 wt.%) Zr alloys were prepared using a vacuum arc-melting furnace. The Ti-25Ta-xZr alloys were then homogenized for 12 hr at 1000 degrees C, followed by water quenching. Formation of the nanotubular oxide surface structure was achieved initially on the Ti-25Ta-xZr alloys by anodization in a 1 M H3PO4 electrolyte containing 0.8 wt.% NaF at room temperature, using a potentiostat. After the first formation of the nanotubes was achieved, this initial nanotube layer was eliminated, and further anodization was carried out repeatedly. The microstructure, phase transformation, and morphology of nanotubular Ti-25Ta-xZr alloys and the process of nanotube growth using this ATO method were analyzed by X-ray diffraction, field-emission scanning electron microscopy, and energy dispersive X-ray spectroscopy. Microstructures of the Ti-25Ta-xZr alloys changed from α" phase to β phase. Nanotubes formed with the ATO technique had pit-like top holes, with thinner walls and lower contact angle, compared to the initially formed nanotubes.