Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Effect of Preoperative Occlusal Matrices on the Vickers Microhardness of Composite Disks Polymerized with QTH and LED
Raquel Castillo-Oyagüe1, Paul J Milward2, Alicia Martín-Cerrato3
1Department of Buccofacial Prostheses, Faculty of Dentistry, Complutense University of Madrid (U.C.M.), Pza. Ramón y Cajal, s/n, Madrid, 28040, Spain.
Purpose:
This study aimed to assess the reliability of the preoperative occlusal matrix technique in terms of the surface Vickers microhardness (VMH) of the underlying composite restorative material.
Materials And Methods:
Two hundred microhybrid composite cylinders were built up and light-cured in a single-layer step, forming two experimental groups (N = 100) according to their heights (1.5 mm/2 mm). Each group was divided into five subgroups (N = 20) depending on the matrix thickness (no matrix/0.5 mm/1 mm/2 mm/3 mm). Half the specimens per subgroup (N = 10) were randomly polymerized with a quartz-tungsten-halogen (QTH) light-curing unit (LCU). The remaining half were cured using a light-emitting diode lamp. The top and bottom samples' sides were tested for VMH at 1 hour and 24 hours post-curing using a universal VMH machine. A multiple analysis of variance with repeated measurements for the "surface" factor and the Student-Newman-Keuls test were run (α = 0.05). Bottom/top microhardness ratios were compared with the empirically accepted limit (0.8). Surface topography was analyzed under a scanning electron microscope.
Results:
The thinnest matrices provided the significantly best VMH values. LCU, disc height, and time also contributed to VMH. At 24 hours, 2-mm high discs polymerized with QTH resulted in inadequate microhardness ratios when 1-mm thick to 3-mm thick matrices were used.
Conclusion:
The thinnest matrices are the most recommendable ones.
Clinical Significance:
The esthetics and occlusal reproducibility achieved with customized occlusal matrices fabricated before cavity preparation have been widely demonstrated. However, their effect on the physical properties of the restorations deserves further investigation. Although more studies are necessary, the thinnest matrices seem to be the most suitable to preserve the composite surface VMH and the curing depth.