Synthesis of pH- and ionic strength-responsive microgels and their interactions with lysozyme

Microgels composed of carboxymethyl cellulose (CMC) polymers via chemical crosslinking with sodium trimetaphosphate were synthesized and characterized using thermogravimetric analysis (TGA), swelling, and rheological analysis. The effects of pH, ionic strength, and crosslinking density on lysozyme loading in microgels were also studied. The microgel particle size ranged primarily from 10 to 20 μm. TGA revealed that the crosslinking increased the thermal stability of CMC. The swelling degree increased as pH increased from 3 to 5, and remained almost constant from pH 5 to 8. However, the swelling degree decreased with increasing ionic strength. The rheological analysis was in good agreement with the results of swelling degree. The protein uptake decreased with increasing ionic strength and crosslinking density. The pH 6 was the optimal pH for lysozyme absorption at ionic strength 0.05 M. The lysozyme-microgel complex was identified by confocal laser scanning microscopy, and the lysozyme distribution in the microgel was observed to be rather homogeneous.