Thermoluminescence properties of gamma-irradiated nano-structure hydroxyapatite

The suitability of nano-structured hydroxyapatite (HAP) for use as a thermoluminescence dosimeter was investigated. HAP samples were synthesized using a hydrolysis method. The formation of nanoparticles was confirmed by X-ray diffraction and average particle size was estimated to be ~30 nm. The glow curve exhibited a peak centered at around 200 °C. The additive dose method was applied and this showed that the thermoluminescence (TL) glow curves follow first-order kinetics due to the non-shifting nature of Tm after different doses. The numbers of overlapping peaks and related kinetic parameters were identified from Tm -Tstop through computerized glow curve deconvolution methods. The dependence of the TL responses on radiation dose was studied and a linear dose response up to 1000 Gy was observed for the samples.