Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking

Wenwen Wang1, Zhiliang Zhang2, Xuechong Ren1

  • 1Corrosion and Protection Centre, Key Laboratory for Environmental Fracture (MOE), University of Science and Technology Beijing, Beijing 100083, China.

Scientific Reports
|June 13, 2015
PubMed

More Related Videos

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

10.2K
Potentiodynamic Corrosion Testing08:43

Potentiodynamic Corrosion Testing

Published on: September 4, 2016

18.6K

Related Concept Videos

Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
66
Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller...
847
Stress Concentrations01:13

Stress Concentrations

The concept of stress concentration is crucial for understanding how materials respond under bending stresses, particularly when there are irregularities or discontinuities in the material's geometry. Normally, stress in a symmetric member subjected to pure bending is assumed to be uniformly distributed across the entire cross-section. However, this assumption does not hold when there are variations in the cross-sectional geometry or the presence of notches and holes.
The stress...
787
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
720
Residual Stresses01:26

Residual Stresses

Residual stresses reside in a structure even after removing the original stress inducer. This phenomenon often arises from varied plastic deformations across different parts of a structure. Consider a rod stretched beyond its yield point. It will not regain its original length due to permanent deformation. Even after load removal, the rod does not entirely lose stress because of uneven plastic deformations, resulting in residual stresses. The computation of these stresses in structures is...
1.0K
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
29.5K