Surface Modification of Li1.2Ni0.13Mn0.54Co0.13O2 by Hydrazine Vapor as Cathode Material for Lithium-Ion Batteries
Jie Zhang1, Zhihong Lei1, Jiulin Wang1
1Shanghai Electrochemical Energy Devices Research Center, Department of Chemical Engineering, Shanghai Jiao Tong University, 800 Dongchuan Road, Shanghai 200240, China.
Abstract:
An artificial interface is successfully prepared on the surface of the layered lithium-rich cathode material Li1.2Ni0.13Mn0.54Co0.12O2 via treating it with hydrazine vapor, followed by an annealing process. The inductively coupled plasma-atomic emission spectrometry (ICP) results indicate that lithium ions are leached out from the surface of Li1.2Ni0.13Mn0.54Co0.12O2 by the hydrazine vapor. A lithium-deficiency-driven transformation from layered to spinel at the particle surface happens in the annealing process, which is proved by the results of X-ray diffraction (XRD) and high-resolution transmission electron microscope (HRTEM). It is also found that the content of the spinel phase increases at higher annealing temperature, and an internal structural evolution from Li1-xM2O4-type spinel to M3O4-type spinel takes place simultaneously. Compared to the pristine Li1.2Ni0.13Mn0.54Co0.12O2, the surface-modified sample annealed at 300 °C delivers a larger initial discharge capacity of 295.6 mA h g(-1) with a Coulombic efficiency of 89.5% and a better rate performance (191.7 mA h g(-1) at 400 mA g(-1)).
Related Concept Videos
01:19Acid Halides to Alcohols: LiAlH4 Reduction
The mechanism proceeds in three steps. First, the nucleophilic hydride ion attacks the carbonyl carbon of the acid halide to form a tetrahedral intermediate. Next, the carbonyl group is re-formed, and the halide ion departs as a leaving group, generating an aldehyde. A second nucleophilic attack by the hydride yields an alkoxide ion, which, upon protonation, gives a primary alcohol as...
00:55Nitriles to Amines: LiAlH4 Reduction
As shown below, the mechanism involves three steps. Firstly, the hydride ion acting as a nucleophile attacks the nitrile carbon to form an anion. In the second step, a second equivalent of the hydride ion attacks the anion to...
01:17Esters to Alcohols: Hydride Reductions
Lithium aluminum hydride is a source of hydride ions and functions as a nucleophile. The mechanism proceeds in three steps. Firstly, the nucleophilic hydride ion attacks the carbonyl carbon of the ester to form a tetrahedral intermediate. Subsequently, the carbonyl group re-forms,...
01:20Amides to Amines: LiAlH4 Reduction
Amide reduction requires two equivalents of the reducing agent, acting as a source of hydride ions. As shown in the figure, the reaction is initiated with a nucleophilic attack by the hydride ion at the carbonyl carbon to form a tetrahedral intermediate.