Electrochemically Synthesized Sb/Sb2O3 Composites as High-Capacity Anode Materials Utilizing a Reversible Conversion...

Sb/Sb2O3 composites are synthesized by a one-step electrodeposition process from an aqueous electrolytic bath containing a potassium antimony tartrate complex. The synthesis process involves the electrodeposition of Sb simultaneously with the chemical deposition of Sb2O3, which allows for the direct deposition of morula-like Sb/Sb2O3 particles on the current collector without using a binder. Structural characterization confirms that the Sb/Sb2O3 composites are composed of approximately 90 mol % metallic Sb and 10 mol % crystalline Sb2O3. The composite exhibits a high reversible capacity (670 mAh g(-1)) that is higher than the theoretical capacity of Sb (660 mAh g(-1)). The high reversible capacity results from the conversion reaction between Na2O and Sb2O3 that occurs additionally to the alloying/dealloying reaction of Sb with Na. Moreover, the Sb/Sb2O3 composite shows excellent cycle performance with 91.8% capacity retention over 100 cycles, and a superior rate capability of 212 mAh g(-1) at a high current density of 3300 mA g(-1). The outstanding cycle performance is attributed to an amorphous Na2O phase generated by the conversion reaction, which inhibits agglomeration of Sb particles and acts as an effective buffer against volume change of Sb during cycling.