Cross-linked κ-carrageenan polymer/zinc nanoporous composite matrix for expanded bed application: Fabrication and...

Expanded bed adsorption (EBA) is a reliable separation technique for the purification of bioproducts from complex feedstocks. The specifically designed adsorbent is necessary to form a stable expanded bed. In the present work, a novel custom-designed composite matrix has been prepared through the method of water-in-oil emulsification. In order to develop an adsorbent with desirable qualities and reduce the costs, κ-carrageenan and zinc powder were used as the polymeric skeleton and the densifier, respectively. The prepared composite matrix was named as KC-Zn. Optical microscope (OM) and scanning electron microscope (SEM) were applied to characterize the morphology and structure of prepared composite matrix. These analyses approved good spherical shape and porous structure with nano-scale pores in the range of about 60-180nm. The results from the particle size analyzer (PSA) revealed that all the KC-Zn beads followed logarithmic normal size distribution with the range of 50-350μm and average diameter of 160-230μm, respectively. Main physical properties of KC-Zn matrices were measured as a function of zinc powder ratio to κ-carrageenan slurry, which showed an appropriate wet density in the range of 1.39-2.27g/ml, water content of 72.67-36.41% and porosity of 98.07-80.24%, respectively. The effects of matrix density and liquid phase viscosity on hydrodynamic behavior of prepared matrix have been investigated by residence time distribution (RTD) experiments in an expanded bed. The results indicated that in a constant liquid velocity as the matrix density was increased, the expansion factor of bed decreased and the axial mixing coefficient increased. Moreover, an enhancement in the fluid viscosity led to an increase in the bed expansion and a decrease in the stability of expanded bed. Therefore using a matrix with higher density seems necessary to face viscous feedstocks. All the results demonstrated that proper physical properties and hydrodynamic characteristics of KC-Zn matrix confirm good potential for possible use in high flow rate expanded bed operations.