Highly Dispersed Gold Nanoparticles Supported on SBA-15 for Vapor Phase Aerobic Oxidation of Benzyl Alcohol

Gold nanoparticles supported on SBA-15 are prepared by homogenous deposition-precipitation method (HDP) using urea as the precipitating agent. The structural features of the synthesized catalysts were characterized by various techniques such as X-ray diffraction (XRD), transmission electron microscopy (TEM), nitrogen adsorption-desorption (BET), pore size distribution (PSD), CO chemisorption and X-ray photoelectron spectroscopy (XPS). The catalytic activity and stability of the Au/SBA-15 catalysts are investigated during the vapor phase aerobic oxidation of benzyl alcohol. The BJH pore size distribution results of SBA-15 support and Au/SBA-15 catalysts reveals that the formation of mesoporous structure in all the samples. TEM results suggest that Au nanoparticles are highly dispersed over SBA-15 and long range order of hexagonal mesopores of SBA-15 is well retained even after the deposition of Au metallic nanoparticles. XPS study reveals the formation of Au (0) after chemical reduction by NaBH4. The particle size measured from CO-chemisorption and TEM analysis are well correlated with the TOF values of the reaction. Au/SBA-1 5 catalysts are found to show higher activity compare to Au/TiO2 and Au/MgO catalysts during the vapor phase oxidation of benzyl alcohol. The catalytic functionality are well substantiated with particle size measured from TEM. The crystallite size of Au in both fresh and spent catalysts were measured from X-ray diffraction.