Effects of Mechanical Methods Used in Peri-implantitis Treatment on Implant Surface Decontamination and Roughness
Published on: March 14, 2025
Surface roughness of dental implants and treatment time using six different implantoplasty procedures
Christian F Ramel1, Anja Lüssi1,2, Mutlu Özcan1
1Clinic of Fixed and Removable Prosthodontics and Dental Material Science, Center of Dental Medicine, University of Zurich, Zurich, Switzerland.
Objectives:
To test whether or not one of six implantoplasty procedures is superior to the others rendering a minimal final implant surface roughness and a short treatment time.
Material And Methods:
Forty-two one-piece implants were embedded in epoxy resin blocks with 6-mm rough implant surface exposed. The following implantoplasty polishing sequences were applied: Brownie(®) , Greenie(®) sequence (BG) (diamond rotary instruments 106-, 40-, 15-μm grit, Brownie(®) , Greenie(®) silicone polishers); Arkansas stone sequence (AS) (diamond 106-, 40-, 15-μm grit, Arkansas stone torpedo-shaped bur); Short diamond sequence (SD) (diamond 106-, 40-, 4-μm grit); Short diamond sequence with Greenie(®) (SDG) (diamond 106-, 40-, 4-μm grit, Greenie(®) ); Complete diamond sequence (CD) (diamond 106-, 40-, 15-, 8-, 4-μm grit); Complete diamond sequence with Greenie(®) (CDG) (106-, 40-, 15-, 8-, 4-μm grit, Greenie(®) ). The polished neck portion served as a positive control, the untreated sandblasted and acid-etched surface as negative control. Each implant was scanned with a contact profilometer rendering Ra values and Rz values as a measure of surface roughness. The time needed to polish the implant surface for each group was recorded. Simultaneous comparisons between more than two groups were done performing Kruskal-Wallis tests. Comparisons between two groups were analysed using Wilcoxon rank-sum tests.
Results:
Mean Ra values amounted to 0.32 ± 0.14 μm (BG), 0.39 ± 0.13 μm (AS), 0.59 ± 0.19 μm (SDG), 0.71 ± 0.22 μm (SD), 0.75 ± 0.26 μm (CDG), 0.98 ± 0.30 μm (CD), 0.10 ± 0.01 μm (PC) and 1.94 ± 0.47 μm (NC). Pairwise one-sided comparisons between the test group revealed statistically significant differences (P < 0.05). The shortest treatment time was recorded for group AS (13 ± 2 min) and the longest for CDG (21 ± 2 min) and BG (21 ± 4 min).
Conclusions:
Considering final surface roughness and treatment duration, the use of rotary diamond burs in decreasing roughness, followed by an arkansas stone (group AS), appears to be an optimal treatment option.