Nitrogen-doped hierarchical porous carbon with high surface area derived from graphene oxide/pitch oxide composite
Yuan Ma1, Chang Ma1, Jie Sheng1
1State Key Laboratory of Separation Membranes and Membrane Processes, School of Materials Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China.
Abstract:
A nitrogen-doped hierarchical porous carbon has been prepared through one-step KOH activation of pitch oxide/graphene oxide composite. At a low weight ratio of KOH/composite (1:1), the as-prepared carbon possesses high specific surface area, rich nitrogen and oxygen, appropriate mesopore/micropore ratio and considerable small-sized mesopores. The addition of graphene oxide plays a key role in forming 4 nm mesopores. The sample PO-GO-16 presents the characteristics of large surface area (2196 m(2) g(-1)), high mesoporosity (47.6%), as well as rich nitrogen (1.52 at.%) and oxygen (6.9 at.%). As a result, PO-GO-16 electrode shows an outstanding capacitive behavior: high capacitance (296 F g(-1)) and ultrahigh-rate performance (192 F g(-1) at 10 A g(-1)) in 6 M KOH aqueous electrolyte. The balanced structure characteristic, low-cost and high performance, make the porous carbon a promising electrode material for supercapacitors.
More Related Videos
12:00Evaluating the Electrochemical Properties of Supercapacitors using the Three-Electrode System
Published on: January 7, 2022
08:59Synthesizing a Gel Polymer Electrolyte for Supercapacitors, Assembling a Supercapacitor Using a Coin Cell, and Measuring Gel Electrolyte Performance
Published on: November 30, 2022