Porous poly (D,L-lactide-co-glycolide) acid/biosilicate^® composite scaffolds for bone tissue engineering

This study evaluated the effects of the Biosilicate^® and poly (D,L-lactic-co-glycolic) acid composites on bone repair in a tibial bone defect model in rats by means of using histological evaluation (histopathological and morphometric analysis) and gene expression analysis. Eighty male Wistar rats (12 weeks old, weighing ±300 g) were randomly divided into two groups: Biosilicate^® group (BG) and Biosilicate^® /PLGA group (BG/PLGA). Each group was euthanized at 3, 7, 14, and 21 days after surgery (n = 10 animals per time point). The main findings showed that the incorporation of PLGA into BG had a significant effect on the morphological structure of the material, accelerating mass loss, decreasing the pH and increasing the calcium release. Furthermore, histologic analysis revealed that the BG/PLGA showed increased material degradation, accompanied by higher bone formation compared to BG, after 21 days of implantation. In addition, qRT-PCR analysis showed that BG/PLGA induced an upregulation of the osteogenic genes related to BMP4, Runx2, ALP, and OC. These results show that the present BG/PLGA composite may be used as a bone graft for inducing bone repair. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 63-71, 2017.