Improvement of J(sc) in a Cu2ZnSnS4 Solar Cell by Using a Thin Carbon Intermediate Layer at the Cu2ZnSnS4/Mo
Fangzhou Zhou1, Fangqin Zeng2, Xu Liu1
1School of Photovoltaic and Renewable Energy Engineering, University of New South Wales , Sydney, New South Wales 2052, Australia.
Abstract:
Back contact modification plays an important role in improving energy conversion efficiency of Cu2ZnSnS4 (CZTS) thin film solar cells. In this paper, an ultrathin carbon layer is introduced on molybdenum (Mo)-coated soda lime glass (SLG) prior to the deposition of CZTS precursor to improve the back contact and therefore enhance CZTS solar cell efficiency. By introducing this layer, the short circuit current (Jsc) and device conversion efficiency increase for both nonvacuum (sol-gel) and vacuum (sputtering) methods. Specifically, for the sol-gel based process, Jsc increases from 13.60 to 16.96 mA/cm(2) and efficiency from 4.47% to 5.52%, while for the sputtering based process, Jsc increases from 17.50 to 20.50 mA/cm(2) and efficiency from 4.10% to 5.20%. Furthermore, introduction of this layer does not lead to any deterioration of either open circuit voltage (Voc) or fill factor (FF).
More Related Videos
09:01Fabrication of Robust Nanoscale Contact between a Silver Nanowire Electrode and CdS Buffer Layer in CuIn,GaSe2 Thin-film Solar Cells
Published on: July 19, 2019
12:21Close-Space Sublimation-Deposited Ultra-Thin CdSeTe/CdTe Solar Cells for Enhanced Short-Circuit Current Density and Photoluminescence
Published on: March 6, 2020