Related Experiment Video

Updated: Apr 1, 2026

Treatment of Ligament Constructs with Exercise-conditioned Serum: A Translational Tissue Engineering Model
08:03

Treatment of Ligament Constructs with Exercise-conditioned Serum: A Translational Tissue Engineering Model

Published on: June 11, 2017

14.2K

Comparative Evaluation of Shear Bond Strength of Luting Cements to Different Core Buildup Materials in Lactic Acid

Siddharam M Patil1, Vikas B Kamble2, Raviraj G Desai3

  • 1Senior Lecturer, Department of Prosthodontics, Crown and Bridge, P.M.N.M. Dental College and Hospital , Bagalkot, Karnataka, India .

Journal of Clinical and Diagnostic Research : JCDR
|October 6, 2015
PubMed
Abstract

Keywords:
EndodonticLuting agentRestoration

More Related Videos

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

948
Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives08:40

Standard Test Method ASTM D 7998-19 for the Cohesive Strength Development of Wood Adhesives

Published on: May 17, 2020

3.6K

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
961
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
761
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
667
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
555
Accelerated Curing of Concrete01:25

Accelerated Curing of Concrete

Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...
591
Titration of a Weak Base with a Strong Acid01:20

Titration of a Weak Base with a Strong Acid

The titration curve of a weak base like ammonia with a strong acid like hydrochloric acid is the mirror image of the titration curve of a weak acid with a strong base.
Using the ICE table and substituting the Kb value, we calculate the initial pH of 50 mL of 0.1 M ammonia to be 11.11. Addition of 25 mL of 0.1 M hydrochloric acid to this solution of ammonia results in a buffer with an equal concentration of ammonia and ammonium ions. The pH of this buffer can be calculated by substituting these...
9.5K