Luminescence studies and infrared emission of erbium-doped calcium zirconate phosphor

The near-infrared-to-visible upconversion luminescence behaviour of Er(3+)-doped CaZrO3 phosphor is discussed in this manuscript. The phosphor was prepared by a combustion synthesis technique that is suitable for less-time-taking techniques for nanophosphors. The starting materials used for sample preparation were Ca(NO3)2.4H2O, Zr(NO3)4 and Er(NO3)2, and urea was used as a fuel. The prepared sample was characterized by X-ray diffraction (XRD). The surface morphology of prepared phosphor was determined by field emission gun scanning electron microscopy (FEGSEM). The functional group analysis was determined by Fourier transform infrared (FTIR) spectroscopy. All prepared phosphors with variable Er(3+) concentrations (0.5-2.5 mol%) were studied by photoluminescence analysis. It was found that the excitation spectra of the prepared phosphor showed a sharp excitation peak centred at 980 nm. The emission spectra with variable Er(3+) concentrations showed strong peaks in the 555 nm and 567 nm range, with a dominant peak at 555 nm due to the ((2)H(11/2),(4)S(3/2)) transition and a weaker transition at 567 nm associated with 527 nm. Spectrophotometric determination of the peak was evaluated by the Commission Internationale de I'Eclairage (CIE) method These upconverted emissions were attributed to a two-photon process. The excitation wavelength dependence of the upconverted luminescence, together with its time evolution after infrared pulsed excitation, suggested that energy transfer upconversion processes were responsible for the upconversion luminescence. The upconversion mechanisms were studied in detail through laser power dependence. Excited state absorption and energy transfer processes were discussed as possible upconversion mechanisms. The cross-relaxation process in Er(3+) was also investigated.