Synthesis of Nitrogen-Doped Graphene Quantum Dots at Low Temperature for Electrochemical Sensing Trinitrotoluene

Nitrogen-doped graphene quantum dots (N-GQDs) are synthesized at low temperature as a new catalyst allowing electrochemical detection of 2,4,6-trinitrotoluene (TNT). N-GQDs are made by an oxidative ultrasonication of graphene oxide (GO) forming nanometer-sized species, which are then chemically reduced and nitrogen doped by reacting with hydrazine. The as-synthesized N-GQDs have an average diameter of ∼2.5 nm with an N/C atomic ratio of up to ∼6.4%. To detect TNT, TNT is first accumulated on N-GQDs modified glassy carbon (N-GQDs/GC) electrode by holding the electrode at a 0 V versus Ag/AgCl for 150 s in an aqueous TNT solution. Next, the N-GQDs/GC electrode with accumulated TNT is transferred to a fresh PBS solution (0.1 M, pH 7.0, without TNT), where the TNT reduction current at -0.36 V versus Ag/AgCl in a linear scan voltammogram (LSV) shows a linear response to TNT concentration in the aqueous solution from 1 to 400 ppb, with a correlation coefficient of 0.999, a detection limit of 0.2 ppb at a signal/noise (S/N) of 3, and a detection sensitivity of 363 ± 7 mA mM(-1) cm(-2). The detection limit of 0.2 ppb of TNT for this new method is much lower than 2 ppb set by the U.S. Environmental Protection Agency for drinking water. Therefore, N-GQDs allow an electrochemical method for assaying TNT in drinking water to determine if levels of TNT are safe or not.