Variations in Crystalline Structures and Electrical Properties of Single Crystalline Boron Nitride Nanosheets

We report the studies of (1) the basic mechanism underlying the formation of defect-free, single crystalline boron nitride nanosheets (BNNSs) synthesized using pulsed laser plasma deposition (PLPD) technique, (2) the variation in the crystalline structure at the edges of the hexagonal boron nitride (h-BN) nanosheets, and (3) the basic electrical properties related to the BNNSs tunneling effect and electrical breakdown voltage. The nanoscale morphologies of BNNSs are characterized using scanning electron microscope (SEM) and high-resolution transmission electron microscope (HRTEM). The results show that each sample consisted of a number of transparent BNNSs that partially overlapped one another. Varying the deposition duration yielded different thicknesses of sample but did not affect the morphology, structure, and thickness of individual BNNSs pieces. Analysis of the SEM and HRTEM data revealed changes in the spatial period of the B3-N3 hexagonal structures and the interlayer distance at the edge of the BNNSs, which occurred due to the limited number of atomic layers and was confirmed further by x-ray diffraction (XRD) study. The experimental results clearly indicate that the values of the electrical conductivities of the super-thin BNNSs and the effect of temperature relied strongly on the direction of observation.