TiO₂ scaffolds in peri-implant dehiscence defects: an experimental pilot study

The primary objective was to assess osseointegration of implants with dehiscence defects grafted with a TiO₂ scaffold. The secondary objective was to assess the performance of the scaffold in terms of mechanical stability and bone fill.

Five minipigs had the mandibular premolars extracted. After healing, two dental implants (SLActive^® , Institut Straumann AG, Basel, Switzerland) with associated semi-cylindrical dehiscence defects (Ø = 6 mm, height = 10 mm) were installed in each quadrant. The defects were grafted with test scaffolds (n = 10) or control autologous bone blocks (n = 10). After 3 months submerged healing, the pigs were euthanized and the sites analysed by microcomputed tomography and histology.

Four minipigs were available for second stage surgery; (n = 9) experimental and (n = 7) control sites. The mean bone-to-implant contact on the defect side was 82% (±10%) and 79% (±11%) in the test and control groups respectively. The mean level of first bone-to-implant contact was more coronal on the defect side in the test group 3.2 mm (±0.4 mm) than in the control group 3.6 mm (±1.1 mm). The defect area occupied by bone within the extent of the scaffold varied, but averaged 37% (±14.6%) whereas the material itself occupied 7.4% (±3.5%).

Within the limitations of the study, the results suggest that the novel synthetic scaffold material perform similar to the autologous bone block control with respect to implant osseointegration. The mechanical properties of the scaffold appeared sufficient to withstand clinical load in the present experimental model.